Features:
1. 100% compostable and biodegradable;
2. Compared with traditional petrochemical plastics per unit weight, more than 75% of petrochemical resources can be saved;
3. Compared to conventional petrochemical plastics per unit weight, more than 60% CO2 emissions can be reduced;
4. No toxic substances such as O-benzene plasticizer and bisphenol A, heavy metal content meets the ROH directive, pollution-free;
5. Industrial Compost, EN13432 and AS 4736/5810 certified;
6. Harmless to human body, comply with FDA food contact standard;
7. Good mechanical properties, applied to general plastic processing facilities;
8. Transparency, softness and degradation time could be adjusted as required.
| Subject | Test Standard | Unit | Value |
| Density | ISO1183 | g/cm3 | 1.2-1.5 |
| Melting Point | DSC, 10ºC/min | ºC | 150-170 |
| Melt Flow Index | ISO1133 | g/10min (190ºC, 2.16kg) | ≤20 |
| Tensile Strength | ISO527 | MPa | ≥40 |
| Elongation at Break | ISO527 | % | ≥5 |
| Bending Strength | ISO178 | MPa | ≥30 |
| Flexural Modulus | ISO178 | MPa | ≥1500 |
Features:
1. 100% compostable and biodegradable;
2. Compared with traditional petrochemical plastics per unit weight, more than 75% of petrochemical resources can be saved;
3. Compared to conventional petrochemical plastics per unit weight, more than 60% CO2 emissions can be reduced;
4. No toxic substances such as O-benzene plasticizer and bisphenol A, heavy metal content meets the ROH directive, pollution-free;
5. Industrial Compost, EN13432 and AS 4736/5810 certified;
6. Harmless to human body, comply with FDA food contact standard;
7. Good mechanical properties, applied to general plastic processing facilities;
8. Transparency, softness and degradation time could be adjusted as required.
| Subject | Test Standard | Unit | Value |
| Density | ISO1183 | g/cm3 | 1.2-1.5 |
| Melting Point | DSC, 10ºC/min | ºC | 150-170 |
| Melt Flow Index | ISO1133 | g/10min (190ºC, 2.16kg) | ≤20 |
| Tensile Strength | ISO527 | MPa | ≥40 |
| Elongation at Break | ISO527 | % | ≥5 |
| Bending Strength | ISO178 | MPa | ≥30 |
| Flexural Modulus | ISO178 | MPa | ≥1500 |